Comparative Study of Semiconductors Bismuth Iodate, Bismuth Triiodide and Bismuth Trisulphide Crystals
| Автори | T.K. Patil1, M.I. Talele2 |
| Приналежність | 1 Smt G.G. Khadse Science, Arts College, Muktainagar, 425306 India 2 P. O. Nahata College, Bhusawal, 425201 India |
| Е-mail | tkp.pratik@gmail.com |
| Випуск | Том 4, Рік 2012, Номер 4 |
| Дати | Одержано 20.03.2012; опубліковано online - 29.12.2012 |
| Посилання | T.K. Patil, M.I. Talele, J. Nano- Electron. Phys. 4 No 4, 04003 (2012) |
| DOI | |
| PACS Number(s) | 72.20. – i, 82.70.Gg, 61.05.C – |
| Ключові слова | Gel grown [Bi(IO3)3], BiI3 and Bi2S3 Crystals, XRD (90) , FTIR (29) , Chemical analysis and electrical conductivity. |
| Анотація |
In the present investigation, crystals of Bismuth Iodate[Bi(IO3)3], Bismuth Iodide[BiI3] and Bismuth- Tri Sulphide [Bi2S3] were grown by a simple gel technique using single diffusion method. The optimum growth conditions were established by varying various parameters such as pH of gel solution, gel concentration, gel setting time, concentration of reactant etc. Gel was prepared by mixing sodium meta silicate (Na2SiO35H2O), glacial acetic acid (CH3COOH) and supernant bismuth chloride (BiCl3) at pH value 4.4 and transferred in glass tube of diameter 2.5 cm and 25 cm in length. The mouth of test tube was covered by cotton plug and kept it for the setting. After setting the gel, it was left for aging. After 13 days duration the second supernant K(IO3), KI3 and H2S water gas solution was poured over the set gel by using pipette then it was kept undisturbed. After 72 hours of pouring the second supernatant, the small nucleation growth was observed at below the interface of gel. The good quality crystals of [Bi(IO3)3], [BiI3] and [Bi2S3] were grown. These grown crystals were characterized by XRD, FTIR, Chemical Analysis and Electrical Conductivity. |
|
Перелік посилань |
Інші статті цього номера
1) Irradiation Effects on Microstructure and Dielectric Properties of Ba[(Mg0.32Co0.02)Nb0.66]O3 [BMCN] Thin Films [04001-1-04001-4]2) Preparation and Characterization of NiO Thin Films by DC Reactive Magnetron Sputtering [04002-1-04002-4]
3) Nonlinear Optical Rectification of Confined Exciton in a ZnO/ZnMgO Strained Quantum Dot [04004-1-04004-5]
4) Preparation and Characterization of Thermally Evaporated Octa Substituted Zinc Phthalocyanine Thin Films [04005-1-04005-5]
5) Optical Properties of MEH-PPV and MEH-PPV/ [6,6]-Phenyl C61-butyric Acid 3-ethylthiophene Ester Thin Films [04006-1-04006-4]
6) Maximum and Minimum Transmittance of a Structure Containing N-Identical Pairs of Left- and Right-Handed Materials [04007-1-04007-5]
7) Study of Some Optical Properties of Mixed SnO2-CuO Thin Films [04008-1-04008-4]
8) Simulation Based Analysis of Temperature Effect on Breakdown Voltage of Ion Implanted Co/n-Si Schottky Diode [04009-1-04009-4]
9) Superconducting State Parameters of Bulk Amorphous Alloys [04010-1-04010-3]
10) Adiabatic, Non-Isothermal Plume Expansion into Vacuum in Terms of Knudsen Layer [04011-1-04011-3]
11) Two Dimensional Coulomb Potential of Confined Excitons in Quantum Well Structures [04012-1-04012-5]
12) Study of Growth, EDAX, Optical properties and Surface Morphology of Zinc Tartrate Crystals [04013-1-04013-4]
13) Особливості залежності коефіцієнта тензочутливості від деформації в металевих плівках [04014-1-04014-4]
14) Джерела кластерного пучка. Частина 2. Формування кластерних пучків у соплових джерелах [04015-1-04015-15]
15) Отримання і оптичні властивості плівок ZnSе [04016-1-04016-5]
16) Модифікований алгоритм обробки тінеграм, отриманих за допомогою кодованих апертур [04017-1-04017-6]
17) Модифікація властивостей вуглецевих плівок для фотоелектричних перетворювачів [04018-1-04018-4]
18) Багатодзеркальний відкритий резонатор з ешелеттним дзеркалом [04019-1-04019-4]
19) Моделювання з перших принципів структури сполуки La0.5Li0.5TiO3 [04020-1-04020-4]
20) Роль ефекту самополяризації та електрон-фононної взаємодії у формуванні енергетичного спектру електрона в наноплівці PbI2, вміщеній у полімер E-MAA [04021-1-04021-6]
21) Процеси релаксації з високозбуджених станів в молекулярних системах на основі метиленового голубого [04022-1-04022-7]
22) Формування гранульованих сплавів (Cu, Co) із рівномірним розподілом магнітних гранул на основі масивів наночастинок Co [04023-1-04023-6]
23) Локалізовані стани поблизу нелінійного оптичного хвилеводу [04024-1-04024-4]
24) Визначення розподілу за розмірами металічних наночастинок золота в гідрозолях зі спектрів плазмонного поглинання [04025-1-04025-4]
25) Магніторезистивні властивості плівкових систем на основі Fe і Gd та Co і Gd [04026-1-04026-5]
26) Моделювання ферорідин в обмежених об’ємах [04027-1-04027-9]
27) Effect of Mg Doping on the Structural and Optical Properties of CdS Nanoparticles Synthesized by co-Precipitation Method [04028-1-04028-5]