Characterization of Precipitates in the 18-1-1 and 18-1-1-5 High-Speed Steels During Tempering After Previous Quenching

Автор(ы) Brahim Chermime , Abdelaziz Abboudi , Hamid Djebaili
Принадлежность

Laboratoire Ingénierie et Sciences des Matériaux Avancés, University of Khenchela, Algéria

Е-mail
Выпуск Том 10, Год 2018, Номер 6
Даты Получено 10.08.2018; в отредактированной форме 07.12.2018; опубликовано online 18.12.2018
Ссылка Brahim Chermime, Abdelaziz Abboudi, Hamid Djebaili, J. Nano- Electron. Phys. 10 No 6, 06009 (2018)
DOI https://doi.org/10.21272/jnep.10(6).06009
PACS Number(s) 77.84.Bw
Ключевые слова Carbides, Retained austenite, Tempering, Secondary hardening, High speed steels.
Аннотация

In this paper the precipitates formed during the tempering after quenching (in salt bath) at temperature 1240 °C for 18-1-1 and 18-1-1-5 high-speed steels are investigated using an analytical transmission electron microscope (A-TEM). The study of this tempering is carried out in isothermal and anisothermal conditions, by comparing the results given by dilatometry and hardness. Tempering is performed in the range of 350-750 °C. Coarse primary carbides retained after heat treatment are of the V-rich MC and W-V-rich M6C types. In turn, it gives a significant influence on the precipitation of dispersive secondary carbides (M4C3 type), that is secondary hardening during tempering. The hardness peak is observed in the tempering range of 500-550 °C (66.8 HRC after a double tempering at 550 °C). It was found out that the cobalt in the concentration limited to about 5 %  results in increasing the effect of the secondary hardening by 2 HRC. Between 700 and 750 °C, the impoverished phase (retained austenite) transforms on heating. In the end, in this temperature range of tempering, other more stable carbides of the M6C and M23C6 types are formed developing at the expense of the carbides M4C3 and M7C3 formed before, which then disappear.