Titanium Carbide Obtained by Magnetron Sputtering of Graphite on Heated Titanium Substrate

Автор(ы) O.E. Kaipoldayev , A.D. Muradov , Y.S. Mukhametkarimov , R.R. Nemkayeva , G.A. Baigarinova , M.B. Aitzhanov , N.R. Guseinov
Принадлежность

Al-Farabi Kazakh National University, 71, Al-Farabi Ave., 050040 Almaty, Kazakhstan

Е-mail qaipolda@gmail.com
Выпуск Том 9, Год 2017, Номер 5
Даты Получено 11.07.2017, в отредактированной форме – 18.08.2017, опубликовано online – 16.10.2017
Ссылка O.E. Kaipoldayev, A.D. Muradov, Y.S. Mukhametkarimov, et al., J. Nano- Electron. Phys. 9 No 5, 05045 (2017)
DOI 10.21272/jnep.9(5).05045
PACS Number(s) 61.50.Nw, 61.66.Fn
Ключевые слова Titanium carbide, Magnetron sputtering (14) , Raman spectroscopy (18) , Transition-metal carbide.
Аннотация Titanium carbide was synthetized by sputtering graphite target on heated titanium substrate by magnetron sputtering process. The obtained samples were characterized by X-ray diffraction (XRD) analysis and Raman spectroscopy, the elemental analysis was made by Energy-dispersive X-ray spectroscopy (EDX). Titanium carbide (TiC) structure was obtained by deposition of sputtered carbon atoms and clusters to the resistively heated titanium substrate surface with temperatures 700 °C, 800 °C, 900 °C and 1000 °C. The XRD analysis showed that the formation of TiC structure is take place when the substrate is heated to 1000 °C. The Raman spectroscopy showed that when the incident power of laser is 100 % (35 mW) the structure is unstable in samples with the substrate temperatures 700 °C, 800 °C and 900 °C and the most stable titanium carbide structure is created when the substrate temperature is 1000 °C.