Plasmon Resonance in A-С : Н Films Modified with Platinum Nanoclusters

Автор(ы) O. Prikhodko, N. Manabaev, N. Guseinov, S. Maksimova, E. Muhametkarimov, S. Mikhailova, E. Daineko
Принадлежность

Al-Farabi Kazakh National University, 71, Al-Farabi Str., 050038 Almaty, Kazakhstan

Е-mail
Выпуск Том 6, Год 2014, Номер 3
Даты Получено 19.05.2014, опубликовано online – 15.07.2014
Ссылка O. Prikhodko, N. Manabaev, N. Guseinov, et al., J. Nano- Electron. Phys. 6 No 3, 03067 (2014)
DOI
PACS Number(s) 81.05.Uw, 68.55.Ln
Ключевые слова Amorphous diamond-like films of hydrogenated carbon (a-C ,  H) modified with platinum, Optical density, Nanoclusters (4) , Plasmon resonance (2) , Extinction section.
Аннотация Optical density spectra of amorphous diamond-like films of hydrogenated carbon modified with platinum impurity (a-C : HPt) have been investigated. a-C : HPt films were prepared by the method of ion plasma magnetron co-sputtering of graphite and platinum in argon-hydrogen atmosphere. Platinum content in the films was varied from 0 to 9 at. %. In the optical spectra of a-C : HPt films with different Pt content the peaks of resonance absorption in the range from 496 to 501 nm were found, whilst in the spectrum of a-C : H films the absorption peak is absent. The appearance of these absorption peaks in a-C : HPt films is explained by resonance plasmon vibrations of free electrons in platinum nanoclusters. The average diameter of the Pt nanoclusters was estimated using electromagnetic theory of Mie, and it is ~ 5 nm.