Growth and Сharacterization of Cd3As2 + MnAs Сomposite

Автор(ы) A.V. Kochura1 , S.F. Marenkin2,3, A.I. Ril’2, A.L. Zheludkevich4, P.V. Abakumov1 , A.F. Knjazev1, M.B. Dobromyslov5
Принадлежность

1 South-West State University, Regional Сentre of Nanotechnology, 94, 50 let Octyabrya St., 305040 Kursk, Russia

2 Institute of General and Inorganic Chemistry of Russian Academy of Sciences, 31, Leninskii Pr., 119991 Moscow, Russia

3 Moscow Institute of Steel and Alloys (National University of Science and Technology), 4, Leninskii Pr., 119049 Moscow, Russia

4 Scientific-Practical Materials Research Centre of the National Academy of Sciences of Belarus, Minsk, Belarus

5 Pacific National University, 136, Tikhookeanskaya St., 680035 Khabarovsk, Russia

Е-mail
Выпуск Том 7, Год 2015, Номер 4
Даты Получено 02.10.2015, опубликовано online – 24.12.2015
Ссылка A.V. Kochura, S.F. Marenkin, A.I. Ril’, et al., J. Nano- Electron. Phys. 7 No 4, 04079 (2015)
DOI
PACS Number(s) 81.15.Dj, 68.55.Nq, 75.70.Ak, 78.30.Hv
Ключевые слова Magnetic composite (2) , Cadmium arsenide (2) , Spintronic materials (5) , Thin solid films, Magnetic clusters.
Аннотация Bulk samples of cadmium arsenide and manganese arsenide alloys were synthesized by crystallization from double-component melt. According to data of differential-thermal and X-ray phase analysis, the nature of the interaction between Cd3As2 and MnAs is eutectic; the melting temperature of eutectic is 855 K. The samples were ferromagnetic with Courier temperature of 320 K. By vacuum-thermal evaporation from the alloy of the composite, films Cd3As2 + MnAs have been obtained. The distribution of the elements in them was uniform and the composition corresponded to the initial composition. The films consisted from nanocrystallites with a size of 20 to 50 nm.