Synthesis and Characterization of Novel Nanocrystalline Zirconium (IV) Tungstate Semiconductor

Автор(и) S. Manoj, B. Beena
Приналежність Department of Chemistry, D.B. College, Sasthamcotta, Kollam, Kerala, India 690 521
Випуск Том 3, Рік 2011, Номер 1, Part 1
Дати Received 04 February 2011, in final form 20 March 2011, published online 23 March 2011
Посилання S. Manoj, B. Beena, J. Nano- Electron. Phys. 3 No1, 179 (2011)
PACS Number(s) 71.20.Be, 68.37.Og
Ключові слова Zirconium (IV) tungstate, Semiconductor (55) , Band Gap (25) , EDS (4) , HRTEM, Zirconia, Tungsten oxide.
Nanocrystalline zirconium (IV) tungstate is prepared by chemical coprecipitation method using ethylene diamine tetra acetic acid as the templating agent. Elemental composition is determined by EDS. The characteristic bonding position is identified using FTIR. XRD is used to find the theoritical value of size and phase identification using JCPDS. Morphology is examined using SEM and HRTEM. UV absorption at 260 nm corresponds to an energy gap of 4.48 eV, characteristic of semiconducting nanoparticles.