Ionizing Radiation Induced Modification of the Copper Nanotubes Structure

Автор(ы) M.V. Zdorovets1,2,3, А.А. Mashentseva1,2, A.L. Kozlovskiy1,2, I.A. Ivanov1, К.К. Kadyrzhanov1,2

1 Institute of Nuclear Physics of the Ministry of Energy of the Republic of Kazakhstan, 1, Ibragimov Str., 050032 Almaty, Kazakhstan

2 L.N. Gumilyov Eurasian National University, 2, Satpayev Str., 010008 Astana, Kazakhstan

3 Ural Federal University named after the first President of Russia B.N. Yeltsin, 19, Mira Str., 620002 Ekaterinburg, Russian Federation

Выпуск Том 9, Год 2017, Номер 6
Даты Получено 30.08.2017, в отредактированной форме – 10.10.2017, опубликовано online – 15.11.2017
Ссылка M.V. Zdorovets, А.А. Mashentseva, A.L. Kozlovskiy, et al., J. Nano- Electron. Phys. 9 No 6, 06017 (2017)
DOI 10.21272/jnep.9(6).06017
PACS Number(s) 61.46.Np
Ключевые слова Irradiation with swift heavy ions, Copper nanotubes, XRD analysis, Track-etched membranes.
Аннотация This work presents research in the study of copper nanotubes (Cu-NTs) electrochemically deposited in pores of PET track-etched membranes and irradiated with accelerated C+3 ions with energy of 1.75 MeV/ nucleon; the fluence of accelerated ions was varied in the range from 1  109 to 5  1011 ion/cm2. The morphology and chemical composition of the un-irradiated samples were elucidated using scanning electron microscopy and energy dispersive analysis. An investigation of crystal structure defects that occur during irradiation of Cu-NTs was carried out by X-ray diffraction technique. XRD patterns of Cu-NT after irradiation with high fluence of C3+ ions show the appearance of the characteristic peaks of the polymorphic modification of carbon with a hexagonal structure related to three-layer rhombohedral -graphite with the R3m (160) space group (PDF 47-1154). The most intense peaks are related to (0015) and (104) Miller indices. The absence on the spectra of peaks characteristic for Cu2C and CuC2 copper carbide compounds indicates that the carbon present in the Cu-NT structure as a solid substitutional solution. The changes in such parameters as the size of crystallites, deformation and stress of the crystal lattice of copper NTs etc. are discussed.