Magnetoresistive and Magneto-optical Effects in Granulare Film Alloys Based on Co, Au and Fe

Author(s) О.V. Fedchenko, S.I. Protsenko , L.V. Odnodvorets , I.V. Cheshko , I.Yu. Protsenko
Affiliations

Sumy State University, 2, Rymskyi-Korsakov Str., 40007 Sumy, Ukraine

Е-mail
Issue Volume 9, Year 2017, Number 4
Dates Received 15 March 2017; published online 27 July 2017
Citation О.V. Fedchenko, S.I. Protsenko, L.V. Odnodvorets, et al., J. Nano- Electron. Phys. 9 No 4, 04011 (2017)
DOI 10.21272/jnep.9(4).04011
PACS Number(s) 75.70.Cn, 81.15.Np
Key words Films based on Co, Au and Fe, Magnetoresistance (5) , Kerr effect (2) , Coercive (3) , Magnetization (18) .
Annotation The results of the study magnetoresistive properties (magnetoresistance) and Kerr effect (Kerr rotation angle versus magnetic field, coercive and magnetization) of three- and four-layer films Au(3)/Co(20)/Fe(70)/S, Au(3)/Co(3)/Au(6)/Fe(20)/S, Au(3)/Fe(20)/Au(6)/Co(3)/S, Au(3)/Fe(3)/Au(6)/Co(20)/S and Au(3)/Co(20)/Au(6)/Fe(3)/S (іn parentheses indicate the thickness in nm), which was condensed in vacuum 10 – 8 Pa on single-crystal (100) MgO and amorphous SiO2/Si substrates. It is established that the film systems implemented anisotropic ferromagnetic resistance with an amplitude from 0.1-0.2 % to 0.5-0.7 %. Based on Kerr measurements was established that the value coercive varies from a few mT to 40 mT. Films on substrates with a (100)MgO with two-axis anisotropy, and on the SiO2/Si – uniaxial magnetic anisotropy.